Home > Injection Molding: Filling, Pressure Maintaining, Cooling, and Demolding
Plastic Injection Molding
Products manufactured using injection molding technology have multiple advantages, including high efficiency, precision, repeatability, flexibility, low cost, and environmental friendliness. They have a wide range of applications from daily necessities to high-precision automotive and aerospace industries.
Injection Molding: Filling, Pressure Maintaining, Cooling, and Demolding
Injection molding is a highly efficient and versatile manufacturing process that has the production of plastic components across various industries, from automotive parts to consumer goods and medical devices, injection-molded products are ubiquitous in our daily lives.
The plastic injection molding process mainly includes four stages: filling, pressure maintaining, cooling, and demolding. These four stages directly determine the molding quality of the product, and these four stages are a complete continuous process.
Plastic Filling
Plastic filling is the first step in the entire injection molding cycle. The time starts from the time when the mold is closed and injection molding begins until the mold cavity is filled to approximately 95%. Generally speaking, the shorter the filling time, the higher the molding efficiency. However, in practice, The molding time or injection speed is restricted by many conditions.
- High-speed Filling
Generally, when plastics are filled at high speed, the shear rate will be high. Due to the thinning effect of the shear force, the viscosity of the plastic will gradually decrease, which will reduce the overall flow resistance; and the influence of local viscous heating will also make the thickness of the plastic cured thinner. Therefore, during the flow control phase, the filling behavior often depends on the size of the volume to be filled.
A simple understanding is that in the flow control stage of plastics, due to high-speed filling, the shear dilution effect of the melt is often very large, and the cooling effect of the thin wall is not obvious, so the effect of speed will prevail.
- Low-speed Filling
The low-speed filling is mainly controlled by heat conduction. When filling at low speed, the shear force is generally low, and the local viscosity will be high, which will lead to greater flow resistance of the liquid. Due to the slow replenishment rate and slow flow of hot plastic, the heat conduction effect is more obvious, and the cold film wall quickly takes the heat away. Coupled with a smaller amount of viscous heating, the thickness of the solidified layer is thicker, which further increases the flow resistance at thinner parts of the wall.
The Packing Stage: Ensuring Dimensional Stability
The packing stage, also known as the second-stage injection or pack-and-hold phase, is a crucial step in the injection molding process. It occurs immediately after the initial filling of the mold cavity with molten plastic material. During this stage, additional molten material is injected into the mold cavity to compensate for the volumetric shrinkage that occurs as the plastic cools and solidifies.
- Importance of Packing
The packing stage plays a vital role in maintaining dimensional stability and preventing defects such as sink marks, voids, and short shots. By applying additional pressure and injecting more material, the packing stage ensures that the mold cavity is filled, resulting in a part with consistent density and minimal internal stresses.
- Packing Pressure and Time
The packing pressure and packing time are critical parameters that must be carefully controlled during this stage. Insufficient packing pressure or a short packing time can lead to incomplete filling and dimensional inaccuracies, while excessive packing pressure or prolonged packing time can cause over-packing, resulting in excessive internal stresses and potential part deformation.
- Gate Freeze-Off
During the packing stage, the gate freeze-off phenomenon occurs, where the molten plastic solidifies at the gate area, sealing off the flow path between the mold cavity and the injection unit. Proper gate freeze-off is essential to prevent backflow and ensure consistent part quality.
The Holding Stage: Maintaining Pressure and Minimizing Defects
Following the packing stage, the holding stage, also known as the cooling or solidification stage, begins. During this phase, the molten plastic within the mold cavity continues to cool and solidify while pressure is maintained to counteract the effects of material shrinkage.
- Importance of Holding Pressure
The holding pressure applied during this stage is crucial for preventing defects such as sink marks, voids, and warpages. As the plastic material cools and shrinks, the holding pressure ensures that the mold cavity remains fully packed, minimizing the formation of internal voids or surface depressions.
- Holding Time and Cooling Rate
The holding time and cooling rate are critical parameters that must be carefully controlled during the holding stage. Insufficient holding time or rapid cooling can lead to premature solidification and incomplete packing, resulting in defects. Conversely, excessive holding time or slow cooling can increase cycle times and potentially cause material degradation.
- Mold Temperature Control
Effective mold temperature control is essential during the holding stage to ensure uniform cooling and solidification throughout the part. Improper temperature control can lead to uneven cooling rates, resulting in internal stresses, warpages, and dimensional inaccuracies.
The Cooling Stage: Achieving Optimal Part Quality
The cooling stage is a critical phase in the injection molding process, as it directly impacts the final part quality, dimensional accuracy, and overall cycle time. During this stage, the solidified plastic part continues to cool within the mold cavity until it reaches the desired ejection temperature.
- Importance of Cooling
Proper cooling is essential to ensure that the part achieves the desired mechanical properties, dimensional stability, and surface finish. Inadequate cooling can lead to warpage, internal stresses, and poor part quality, while excessive cooling can increase cycle times and energy consumption.
- Cooling Time and Cycle Efficiency
The cooling time is a crucial factor that affects the overall cycle efficiency of the injection molding process. Optimizing the cooling time can lead to increased productivity and reduced energy consumption while maintaining part quality and dimensional accuracy.
- Cooling Channel Design
The design and placement of cooling channels within the mold play a significant role in achieving uniform cooling and minimizing potential defects. Effective cooling channel design ensures even heat dissipation throughout the mold cavity, preventing hot spots or uneven cooling that can lead to warpages or internal stresses.
- Mold Material and Insulation
The choice of mold material and the use of insulation can influence the cooling rate and overall thermal management during the cooling stage. Materials with high thermal conductivity, such as beryllium-copper alloys, can facilitate efficient heat transfer, while insulation can help maintain consistent mold temperatures and prevent heat loss.
The Ejection Stage: Ensuring Efficient Part Removal
The ejection stage is the final step in the injection molding process, where the solidified and cooled part is removed from the mold cavity. This stage is crucial for ensuring efficient part removal without causing damage or deformation to the part of the mold.
- Importance of Ejection
Proper ejection is essential for maintaining part quality, preventing damage to the mold, and ensuring consistent cycle times. Inefficient ejection can lead to part deformation, surface defects, or even mold damage, resulting in costly downtime and repairs.
- Ejector Pin Design and Placement
The design and placement of ejector pins play a critical role in the ejection stage. Properly designed and positioned ejector pins ensure an even distribution of ejection forces, minimizing the risk of part deformation or damage during ejection.
- Ejection Force and Speed
The ejection force and speed must be carefully controlled to prevent part deformation or damage. Excessive ejection force can cause part distortion or mold damage, while insufficient force can lead to incomplete ejection or part sticking.
- Mold Release Agents and Surface Treatments
The use of mold release agents and surface treatments can facilitate efficient part ejection by reducing friction and adhesion between the part and the mold cavity. However, these agents and treatments must be carefully selected and applied to avoid potential contamination or adverse effects on part quality.
- Automated Part Removal and Handling
In high-volume production environments, automated part removal and handling systems can improve efficiency and consistency during the ejection stage. These systems can include robotic arms, conveyors, or other automated mechanisms to safely and efficiently remove parts from the mold and transfer them for further processing or packaging.
Mastering the crucial stages of packing, holding, cooling, and ejection is essential for achieving consistent quality and optimal performance in injection molding. By understanding the importance of each stage and carefully controlling the critical parameters, manufacturers can produce high-quality parts that meet the stringent requirements of various industries.
Related News
Applied’s expertise in modifying materials at atomic levels and on an ihdustrial scaleenables our customers to transform possibilities into reality.